| Nama merek: | DLX |
| Nomor Model: | Kawat Paduan FeCrAl 0Cr25Al5 |
| MOQ: | 10KG |
| Ketentuan Pembayaran: | L/C,D/A,D/P,T/T,Western Union |
| Kemampuan Pasokan: | 500 ton per bulan |
| 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | Komposisi Kimia (%) - Cr | 12.0-15.0 |
|---|---|---|---|---|---|---|---|
| 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 | Komposisi Kimia (%) - Al | 4.0-6.0 |
| 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | Komposisi Kimia (%) - Re | 5.0-7.0 | 6.0-7.0 | Komposisi Kimia (%) - Re | Sesuai Kebutuhan |
| Sesuai Kebutuhan | Sisa | Sisa | Sisa | Sisa | Sisa | Sisa | Sisa |
| Sisa | 950 | 950 | 950 | 950 | 950 | 950 | 950 |
| 1250 | 1250 | 1350 | 1350 | 1350 | 1400 | Resistivitas pada 20°C (μΩ.m) | 1.25 |
| 1.42 | 1.42 | 1.23 | 1.23 | 1.45 | 1.53 | Kepadatan (g/cm³) | 7.4 |
| 7.1 | 7.16 | 52.7 | 7.35 | 7.1 | 7.1 | 52.7 | 52.7 |
| 46.1 | 63.2 | Koefisien Ekspansi Linier (αx10⁻⁶/°C) | 46.9 | 46.1 | -- | Koefisien Ekspansi Linier (αx10⁻⁶/°C) | ≥80/1300 |
| 16 | 14.7 | 1450 | 13.5 | 16 | 16 | 1450 | 1450 |
| 1500 | 1500 | 1520 | 1520 | 1520 | 1520 | Kekuatan Tarik (N/mm²) | 580-680 |
| 630-780 | 630-780 | 650-800 | 650-800 | 650-800 | 680-830 | Perpanjangan saat Putus (%) | >16 |
| >12 | >12 | Variasi Luas (%) | Variasi Luas (%) | Variasi Luas (%) | Variasi Luas (%) | Variasi Luas (%) | 65-75 |
| 60-75 | >5 | 65-75 | >5 | >5 | >5 | >5 | >5 |
| >5 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| 200-260 | -- | -- | -- | -- | -- | -- | -- |
| ≥80/1300 | ≥80/1300 | ≥80/1350 | ≥80/1350 | ≥80/1350 | ≥80/1350 | Ferrit | Ferrit |
| Ferrit | Magnetik | Magnetik | Magnetik | Magnetik | Magnetik | Magnetik | Magnetik |
| Magnetik | Bentuk | Bentuk | Bentuk | Bentuk | Bentuk | Bentuk | Bentuk |
| Kawat | 0.05-7.5 |
|---|---|
| Batang | 8-50 |
| Pita | (0.05-0.35)*(0.5-6.0) |
| Strip | (0.5-2.5)*(5-180) |
| Fitur & Keunggulan Utama | Ketahanan Oksidasi yang Sangat Baik |